Water Retention Behaviour and Fracture Toughness of Coir/Pineapple Leaf Fibre with Addition of Al2O3 Hybrid Composites under Ambient Conditions

Due to their high mechanical and physical properties, natural fibre-based composite materials have been important in many fields of application for four to five years. The chief intention of the current study is to determine the mechanical and water retention features of composite materials under ambient conditions. Coir and pineapple leaf fibre were used as a reinforcement, aluminium oxide as additives, and polyester as a matrix. The hybrid resources were laminated by the manual hand lay-up method. The mechanical characteristics like tensile, flexural, and fracture toughness properties were tested as per the ASTM standard. Nanoparticle weight ratio and its size variation significantly impact mechanical qualities. The hybrid composite’s water retention behaviour was tested for two types of water levels: ordinary tab water and nanofluid. The moisture uptake of the composites rose as the fibre volume increased, and after 640 hours, all of the composites had reached equilibrium. According to the results, the following combinations have the maximum mechanical strength: 15% wt.% coir, 15% wt.% pineapple, 10% wt.% nanofiller, and 60% wt.% polyester resin. The combinations mentioned above withstand the most load during the tests. Compared to 20% filler, 10% Al2O3 filler produces good interfacial adhesion in the current study. The fractured specimens were analyzed using scanning electron microscopic (SEM) pictures to recognize better the failure process of composites during mechanical testing.